yield strength的例句大全

The yield strength ( σ0.2 ) , ultimate tensile strength ( σ b ) and elongation ( δ ) of A 356-T 6 alloy were 240 MPa, 254.8 MPa and 1.16 % , respectively.

屈服强度 、 抗拉强度和伸长率分别为240MPa 、 254.8MPa和1.16%.

互联网摘选

The V-N microalloy steel with yield strength of 550 MPa is produced by EAF-CSP route.

目前,在EAF-CSP 流程中通过V -N 微合金化技术可成功生产屈服强度为550MPa的高强度低合金钢.

互联网摘选

Desirable properties for forming include low yield strength and high ductility.

令人满意的成形特性包含了低降伏应力和高延展性.

互联网摘选

The yield strength fy of reinforcement is used in design.

在设计中利用的是钢筋的屈服强度.

互联网摘选

Oxgen precipitates ( useful for gettering ) can reduce the yield strength ( critical shear stress ) up to fivefole.

氧沉淀 ( 可用作吸杂 ) 会使屈服强度 ( 临界剪应力 ) 降低为五分之一.

词典精选例句

Dislocation strengthening and grain refinement strengthening makes coil 059 with the higher yield strength.

位错强化与晶粒细化强化是059板卷具有高屈服强度的原因.

网络文摘精选

FIG. 5 shows the average yield strength as a function of extrusion speed and location.

图5示出了平均屈服强度与挤压速度和位置的关系.

互联网摘选

The results show that the steel has high yield strength and quality forming property.

结果表明,研制开发出的铌钛微合金化IF钢具有高的屈服强度和优良的成形性能.

互联网摘选

The yield strength, tensile ratio and toughness are major quality indexes of steel pipe ( board ).

屈服强度 、 屈强比、韧性等是钢管 ( 板 ) 的主要质量指标,合理确定这些指标的数值有相当难度.

互联网摘选

CuPTiRE anti-erosion hot rolling stripes are divided into two grades in yield strength : 295 MPa, 345 MPa.

09CuPTiRE耐大气腐蚀热轧钢板按屈服强度分为295MPa级和345MPa级两个级别.

互联网摘选

The creep rate was increased while the yield strength was reduced by anodic dissolution.

阳极电流不但使恒载荷下的不锈钢蠕变速度增加,而且使屈服强度下降.

互联网摘选

Residual stress concentration a notch depends on both notch geometry and yield strength of the material.

缺口根部的残余应力存在应力集中效应,应力集中值不仅取决于缺口几何形状而且和材料的屈服强度有关.

互联网摘选

The results showed that tensile strength, tensile yield stress and tensile breaking stress were increased with the increase of bore distance;

结果表明，随筛板孔距的增加，其拉伸强度、拉伸屈服应力及拉伸断裂应力均提高；

互联网摘选

The yield strength in tension and vicat softening temperature were both increased with the increase of chlorinity.

改性PVCC的拉伸屈服强度和维卡软化点均随氯含量的增加而提高；

互联网摘选

The influence of thermal oxygen on the tensile yield stress, tensile breaking stress, impact strength, elongation at break, melt point and the heat of melting of PF Nylon 1212 is investigated.

通过热氧老化试验，考察了热氧对尼龙1212拉伸屈服应力、拉伸断裂应力、冲击强度、断裂伸长率、熔点、熔融热的影响。

互联网摘选

It is investigated that the influence of Bauschinger Effect on yield strength of tube body by using four point bending test to simulate the tube making process at varying stress strain amplitudes.

采用X65钢板在四点弯曲加载条件下，模拟输油管制管过程中不同应变量下的应力&应变过程，研究包申格效应对输油管管体屈服强度的影响。

互联网摘选

Fiber model is used to calculate the interaction of biaxial bending deformation in reinforced concrete columns. The effect of the system parameters on inelastic torsional response is evaluated: stiffness eccentricity es, yield strength eccentricity ep and lateral period T.

以纤维模型模拟双向地震作用下混凝土柱的双轴弯曲，考查刚度偏心es、强度偏心ep和自振周期T等因素对结构扭转的影响。

互联网摘选

Although the stress level is below the yield strength, long-term exposure to the alternating stresses may make the platform suffer the suddenly fatigue damage.

虽然应力水平远低于材料的屈服强度，但是在长期的交变应力作用下，桩腿有可能产生突然性的疲劳破坏。

互联网摘选

The yield strength is reduced by 10~ 20 MPa after natural ageing and it can be simulated by artificial ageing ( 100 ℃× 2h or 200 ℃× 1h).

自然时效后屈服强度下降10～20MPa，用人工时效可以模拟自然时效，工艺是100℃×2h或200℃×1h。

互联网摘选

, and YS ( yield strength) and the value of YS/ UTS increase through the followed artificial ageing with obvious loss of elongation.

而其后的人工时效处理能明显提高合金的屈服强度和屈强比，但也明显降低了延伸率。

互联网摘选